Crown reinforcement for a radial tire

ABSTRACT

A tire P, comprising a radial carcass reinforcement surmounted radially by a crown reinforcement consisting of at least one working reinforcement formed of at least two plies of calendered inextensible metallic reinforcement elements, of rubber mix, which are parallel to each other within each ply and are crossed from one ply to the next, forming with the circumferential direction angles α 1 , and α 2  of between 10° and 45°, said working plies having axial widths L 1  and L 2 , and of at least one supplementary ply, referred to as a protective ply, of axial width L 3  such that L 2 &lt;L 3 , L 2  being the width of the working ply adjacent to the protective ply, and comprising metallic reinforcement elements. According to the invention, a layer P of cohesive rubber mixes is arranged between at least the ends of the working crown plies.

This application is a U.S. Continuation Application under 35 USC 371 of International Application PCT/EP2004/001354 filed Feb. 13, 2004.

The present invention relates to a tire having a radial carcass reinforcement, which is intended to be fitted on heavy vehicles such as lorries, buses, tractors, trailers etc., and relates more particularly to the crown reinforcement of such a tire.

Generally, the radial carcass reinforcement of the tire in question, which is formed of inextensible reinforcement elements made of metal or of aromatic polyamide, is surmounted radially by a crown reinforcement comprising a plurality of crown plies; in particular a triangulation ply formed of metallic elements which are oriented relative to the circumferential direction by a large angle of between 45° and 90°, said triangulation ply in turn being surmounted by two working plies formed of inextensible metallic reinforcement elements which are parallel to each other within each ply and are crossed from one ply to the next, forming angles of between 10° and 45° with the circumferential direction. Said working plies, which form the working reinforcement, may also be covered by at least one so-called protective ply, formed of generally metallic, extensible reinforcement elements, which are referred to as elastic elements.

Cables are said to be inextensible when said cables have a relative elongation at most equal to 0.2% under a tensile force equal to 10% of the breaking load.

Cables are said to be elastic when said cables have a relative elongation at least equal to 4% under a tensile force equal to the breaking load.

The circumferential direction of the tire, or longitudinal direction, is the direction corresponding to the periphery of the tire and defined by the direction of rolling of the tire.

The transverse or axial direction of the tire is parallel to the axis of rotation of the tire.

The radial direction is a direction intersecting and perpendicular to the axis of rotation of the tire.

The axis of rotation of the tire is the axis around which it rotates in normal use.

A radial or meridian plane is a plane containing the axis of rotation of the tire.

The circumferential median plane, or equatorial plane, is a plane perpendicular to the axis of rotation of the tire and which divides the tire into two halves.

In the case of tires for “heavy vehicles”, a single protective ply is usually present and its protective elements are in most cases oriented in the same direction and at the same angle in absolute value as those of the reinforcement elements of the radially outermost and hence radially adjacent working ply. In the case of construction-vehicle tires which are intended to travel on relatively bumpy roads, the presence of two protective plies is advantageous, the elastic elements being crossed from one ply to the next and the reinforcement elements of the radially inner protective ply being crossed with the inextensible reinforcement elements of the radially outer working ply adjacent to said radially inner protective ply.

Application JP 59/118 507, with the aim of avoiding separation between crown plies, shows such a reinforcement structure with a radially outer ply on one hand formed of high-modulus textile reinforcement elements forming with the circumferential direction an angle which in absolute value is smaller than the angle formed by the elements of the radially outer working ply, and on the other hand having an axial width greater than the width of said working ply, while remaining less than the width of the radially inner working ply.

Application JP 03/262 704, with the same aim, describes and shows a solution very close to the previous one as far as the axial widths of the plies and angles of the reinforcement elements of said plies are concerned. Furthermore, it specifies that the radially outermost ply has an elongation at break of at least 5%.

With the aim of protecting the working plies from corrosion, and avoiding separation between the crown reinforcement and tread, document JP 04/055 104, which adopts practically the same axial widths of crown plies, advocates using reinforcement elements of aromatic polyester for the protective ply.

French Patent 2 493 236, with the aim, it would seem, of solving the problems posed by travel on a rough road, advocates a structure similar to the previous ones, but with use in the radially inner and outer plies of reinforcement elements, the elongation at break of which is greater by at least 40% than the elongation at break of the reinforcement elements of the two working plies.

The progress made in terms of length of life (number of kilometers traveled) on wear of “heavy-vehicle” tires, and also the possibility of easy, economical subsequent retreading, requires a crown reinforcement, the resistance to separation between the edges of working plies of which is improved.

Patent FR 2 800 672, in order to limit separation at the ends of working plies, claims a crown reinforcement structure in which a ply, referred to as a protective ply, has an axial width between those of the working crown plies, the reinforcement elements of the protective ply being inclined in the same direction as the reinforcement elements of the radially adjacent working ply and forming with the circumferential direction an angle greater, by at least 5°, than that of said radially adjacent working ply.

In their research and in particular during research into the production of “heavy-vehicle” tires having an increasingly long wear life (number of kilometers traveled), the inventors set themselves the task of defining a tire crown structure which makes it possible to obtain a resistance to separation between the edges of working plies which is improved still further.

This object has been achieved according to the invention by a tire comprising a radial carcass reinforcement radially surmounted by a crown reinforcement consisting of at least one working reinforcement formed of two plies of calendered inextensible metallic reinforcement elements, of rubber mix which are parallel to each other within each ply and are crossed from one ply to the next, forming angles α₁ and α₂ of between 10° and 45° with the circumferential direction, said working plies having axial widths L₁ and L₂, and of at least one supplementary ply, referred to as a protective ply, of axial width L₃ such that L₂<L₃, L₂ being the width of the working ply adjacent to the protective ply, and comprising metallic reinforcement elements, said crown reinforcement furthermore comprising, arranged between at least the ends of the working crown plies, a layer P of cohesive rubber mixes.

A cohesive rubber mix is a rubber mix which is particularly resistant to cracking.

A tire such as has been defined above according to the invention, that is to say having a crown reinforcement such as described, makes it possible to reduce still further the risks of separation between the edges of working plies and thus to improve the life of the tire by permitting in particular retreading thereof. The layer P of rubber mixes makes it possible to obtain decoupling of said working plies, which, in combination with the supplementary ply referred to as a protective ply, leads to an improvement in the resistance to separation between the edges of working plies.

According to an advantageous variant of the invention, the width L₃ of the protective ply is such that L₃<L₁. In other words, the protective ply has an axial width less than the axial width of the radially inner working crown ply and therefore lies between the axial widths of the two working crown plies. During the research, it was demonstrated that it was in particular preferable to avoid the ends of the protective ply and of the radially inner working crown ply axially coinciding. Such a structure would be harmful with regard to the separation between the edges of the two working crown plies.

Advantageously also, independently of the above relationship between the axial widths of the radially inner working crown ply and the protective crown ply, the axial width of the radially inner working crown ply is greater than the axial width of the radially outer working crown ply. In other words, the widths L₁ and L₂ of the working crown plies advantageously satisfy the relationship: L₁>L₂.

According to one preferred embodiment of the invention, the layer P, at the axially outer end of the radially outer working crown ply, has a thickness such that the radial distance d between the two working crown plies, separated by said layer P, satisfies the relationship: 3/5.φ₂ <d<5.φ₂ where φ₂ is the diameter of the reinforcement elements of the radially outer working crown ply.

The distance d is measured from cable to cable, that is to say between the cable of a first working ply and the cable of a second working ply. In other words, this distance d covers the thickness of the layer P and the respective thicknesses of the calendering rubber mixes, which is radially external to the cables of the radially inner working ply and radially internal to the cables of the radially outer working ply.

More preferably still according to the invention, the radial distance between the two working crown plies, separated by the layer P, being equal to d, at the end of the radially outer working crown ply, the end of the supplementary ply, referred to as a protective ply, is separated radially from the working crown ply of width L₁ by the layer P by a distance d′, such that: d≦d′<d+4.φ₂.

The distance d′, like the distance d previously, is measured from cable to cable.

Said distance d′ is greater than or equal to d such that the end of the protective ply is not stressed owing to the proximity of the reinforcement elements of the radially inner working ply. The layer P of rubber mixes advantageously acts as a decoupling layer between the radially inner working ply and the protective ply.

The same distance d′ is preferably less than a distance corresponding to the distance d increased by four times the diameter of the reinforcement elements of the radially outer working layer; beyond such a value, the distance d′ might result in difficulties in retreading operations, resulting in particular in the risk of damage to the crown reinforcement and hence in the impossibility of retreading the tire, because usually the worn tread is removed to a thickness relatively close to the crown reinforcement, which consequently has to satisfy maximum radial positioning conditions such that it is not damaged during said removal of the worn tread.

In the same manner as previously, the radial distance between the two working crown plies, separated by the layer P, being equal to d, at the end of the radially outer working crown ply, the end of the radially inner working crown ply is advantageously distant from the supplementary ply, referred to as a protective ply, by a distance d″, such that d″≧d. Once again, and more specifically in the case of a protective ply the width L₃ of which is greater than the width L₁ of the radially inner working ply, the layer P of rubber mixes advantageously acts as a decoupling layer between the radially inner working ply and the protective ply, such that the ends of the reinforcement elements of the radially inner working ply are not stressed owing to the excessive proximity of the reinforcement elements of the protective ply. In other words, the reinforcement elements of the protective ply advantageously do not penetrate a circle of radius d centered on the end of the reinforcement elements of the radially inner working ply.

The distance d″, like the distances d and d′ previously, is measured from cable to cable.

According to a preferred embodiment of the invention, in particular to ensure sufficient drift rigidity of the tire, the widths of the working crown plies satisfy the relationship: 1>L₂/L₁≧2/3.

More preferably still according to the invention, the axial width D of the layer P between the axially inner end of said layer P and the end of the radially outer working crown ply is such that: 3.φ₂≦D≦20.φ₂. Such a relationship defines a zone of engagement between the layer P of rubber mixes and the radially outer working ply. Such an engagement below a value equal to three times the diameter of the reinforcement elements of the radially outer working ply may not be sufficient to achieve decoupling of the working plies to obtain in particular attenuation of the stresses at the end of the radially outer working ply. A value of this engagement greater than twenty times the diameter of the reinforcement elements of the radially outer working ply may result in an excessive reduction of the drift rigidity.

More preferably still, the axial width D is greater than five times the diameter of the reinforcement elements of the radially outer working ply.

One preferred embodiment of the invention provides for the reinforcement elements of the protective ply to be inclined in the same direction as the reinforcement elements of the radially adjacent working ply, forming with the circumferential direction an angle α₃ of the same direction and greater than or equal to the angle α₂ of the reinforcement elements of said working ply adjacent to the protective ply.

Preferably, the angle α₃, formed by the reinforcement elements of the protective ply with the circumferential direction, is greater than or equal in absolute value to the angle α₂ of the elements of said radially adjacent working ply by at least 5°.

More preferably still, the angular difference α₃−α₂ is at most equal to 20°.

If said difference is less than 5°, the resistance to separation between working plies is not improved; if the difference is greater than 20°, it is possible that the separation between the edges of the two working plies will be adversely affected, contrary to what is desired. The angle α₃ is more advantageously less than 45°.

In an advantageous variant of the invention, the crown reinforcement is finished off, radially between the carcass reinforcement and the working reinforcement, by a triangulation ply formed of inextensible metallic elements, preferably forming with the circumferential direction an angle α₀ of the same direction as the angle α₁ formed by the reinforcement elements of the radially innermost working ply and of between 45° and 90°.

As is known per se, the addition between the working reinforcement and carcass reinforcement of what is called a triangulation ply may be advantageous, said ply being formed of metallic elements inclined greatly relative to the circumferential direction, and preferably having an axial width L₀ which is less than the width L₁ of the radially inner working crown ply.

According to one advantageous embodiment of the invention, in particular intended for “heavy-vehicle” applications, the protective ply is formed of steel cables which are extensible or referred to as elastic. Such metallic reinforcement elements of the protective ply advantageously have a relative elongation at least equal to 4% at break.

According to a first variant of the invention, the layer P of rubber mix is such that the modulus of said layer is identical in the different zones of said layer in contact with the calendering mixes of the two working crown plies in contact therewith.

According to another variant of the invention, the layer P of rubber mixes is formed of a stack of at least two layers of rubber mixes P₁ and P₂ of respective elasticity modules MP₁ and MP₂, at 10% elongation, selected advantageously such that MP₁>MP₂, the radially outermost mixture P₁ being in contact with the radially outermost working crown ply. Such an embodiment of the invention permits a reduction in the stresses on the layer of rubber mix P₁ in contact with the radially outer working crown ply relative to the stresses on the layer of rubber mix P₂. Such an embodiment also makes it possible to improve the resistance to separation between the ends of the working crown plies.

According to this variant embodiment of the invention, the axially outer end of the layer of rubber mix P₂ is preferably axially internal to the end of the radially inner working crown ply, so as not to harm the resistance to separation of said end of the radially inner working crown ply. The axially inner end of said layer of rubber mix P₂ is for its part advantageously axially external to the axially inner end of the layer of rubber mix P₁.

Another variant of the invention also provides for the layer P of rubber mixes to be formed of a stack of at least two layers of rubber mixes P₁ and P₂ of respective elasticity moduli MP₁ and MP₂, at 10% elongation, such that MP₁<MP₂, the radially outermost mixture P₁ being in contact with the radially outermost working crown ply.

According to another advantageous embodiment of the invention, said tire comprises a layer of cohesive rubber mix GB radially to the inside of the working reinforcement, the axially outer end of said layer GB being at a distance from the equatorial plane greater than L₁/2.

According to this other embodiment of the invention, when the crown reinforcement comprises a triangulation ply radially between the carcass reinforcement and the working reinforcement, the layer of rubber mix GB is either radially internal to said triangulation ply, or radially, at least in part between, the radially inner working crown ply and the triangulation ply, and hence advantageously in contact with the radially inner working crown ply and in contact with the triangulation ply, the latter preferably being axially narrower than the radially inner working crown ply. The tests carried out during the research have shown that such a layer of rubber mix GB also contributes to improving the resistance to separation of the ends of the working crown plies.

Another advantageous embodiment of the invention further provides, in particular to limit the risks of degradation of the tires due to the formation of cracks between the ends of the reinforcement elements of the working plies and to the propagation thereof, at least in each shoulder, a ply of reinforcement elements, advantageously of small diameter, which are parallel to each other in the ply and forming with the circumferential direction an angle of between 70 and 110°, the axially inner edge of said additional ply being radially adjacent to at least one edge of one of the plies of the crown reinforcement, and the axially outer edge of said additional ply preferably being radially internal to the edge of the ply to which the additional ply is adjacent.

The edge of a ply is defined as a limited zone of the ply defined axially by one end of said ply.

One advantageous embodiment of the invention provides for the reinforcement elements of the additional shoulder ply to be what is referred to as of small diameter, compared with the compacted diameter of the metallic elements of the working crown plies of the tire, when said compacted diameter is less than 0.5 times the compacted diameter of the metallic elements of the working crown plies of the tire.

More preferably still, the compacted diameter of the reinforcement elements of the additional ply is less than 1 mm.

The compacted diameter is the measured diameter of a reinforcement element when the cords forming it are in contact with each other.

These diameters of the reinforcement elements of the additional ply allow the presence of said ply without said reinforcement elements, and more particularly their ends, being a new source of risk of degradation within the tire.

It appears that a ply of this type produced in accordance with the invention very significantly improves the resistance of the tire to impacts affecting the shoulder.

The reinforcement elements of the additional ply may be of textile or metallic type.

According to one advantageous embodiment of the invention and more particularly in the case of an additional shoulder ply, the axially outer edge of which is located at least in the radially upper part of the zone of the sidewall, the reinforcement elements of said additional ply are metallic; it would appear that the tire according to the invention then meets another requirement, because a tire thus produced makes it possible to limit the risks of degradation due to the generation of heat appearing owing to the hysteresis of the elastomers without furthermore adversely affecting the other desired properties of the rubbers or more directly of the tires.

Said reinforcement elements are then, more preferably still, made of steel, steel being recognized as being a very good conductor of heat.

The tire according to the invention, by the presence of the additional plies located at the shoulders, permits rapid evacuation of the heat produced during travel towards the outer surface of the tire, because the positioning of the additional plies makes it possible to conduct the heat towards the sidewall zones where the rubber mass is less great and therefore permits more rapid evacuation of heat even if the nature of the rubber is not more favorable to good conduction; the low thickness in fact enables the heat to be eliminated more rapidly, the path to be traveled being short from the heart of the rubber mass towards the outer surface. The tire according to the invention thus makes it possible to reduce the operating temperatures which might lead to a reduction in the life of the tires.

According to a preferred embodiment of the invention, the additional ply has its axially inner edge adjacent radially to the outside to the edge of the protective ply.

According to this embodiment of the invention, the additional ply is advantageously in contact with the layer of rubber mix P which makes it possible to decouple the free ends of the reinforcement elements of the different working plies.

Furthermore, the axially outer edge of the additional shoulder ply is for its part advantageously axially adjacent to the profiled element of rubber mix, one of the wings of which, as is known per se, provides the join between the carcass reinforcement and the edges of the radially innermost crown reinforcement plies, and the other wing of which passes down into the sidewall.

According to this latter embodiment, the additional ply makes it possible on one hand to limit the formation and the propagation of cracks in the zones of the ends of the reinforcement elements and, on the other hand, to provide protection from the risks linked to impacts on the sidewall zones. Furthermore, the additional ply permits evacuation of the heat generated in the shoulder zone.

The invention also provides for combining all the aforementioned different embodiments or at least two thereof, in particular the use of a layer P of rubber mixes consisting of a stack of at least two layers of rubber mixes P₁ and P₂ and/or the use of a layer of rubber mix GB and/or the use of a ply of reinforcement elements of small diameter in each shoulder.

Other advantageous details and characteristics of the invention will become apparent hereafter from the description of the examples of embodiment of the invention with reference to FIGS. 1 to 5, which represent:

FIG. 1: a partial view in meridian section of a diagram of a tire according to one embodiment of the invention,

FIG. 2: a partial view in meridian section of a diagram of a tire according to a second embodiment of the invention,

FIG. 3: a partial view in meridian section of a diagram of a tire according to a third embodiment of the invention,

FIG. 4: a partial view in meridian section of a diagram of a tire according to a fourth embodiment of the invention,

FIG. 5: a partial view in meridian section of a diagram of a tire according to a fifth embodiment of the invention.

The figures are not shown to scale in order to simplify understanding thereof.

FIG. 1 shows a partial diagrammatic view in meridian section of a tire 1 of dimension 385/65.R.22.5 X. FIGS. 1 to 5 show only a half-view of the tires which are extended symmetrically to the axis XX′ which represents the circumferential median plane, or equatorial plane, of a tire.

The tire 1 comprises a radial carcass reinforcement composed of a single ply 2 of inextensible metal cables, that is to say, cables which have an elongation of at most 0.2% under a tensile force equal to 10% of the breaking load. Said carcass reinforcement is anchored within each bead; said beads are not shown in FIGS. 1 to 5. It is surmounted, radially to the outside, by a crown reinforcement 3 comprising radially from the inside to the outside:

a first crown ply 30 referred to as a triangulation ply, formed of inextensible metal cables made of steel, which are oriented at an angle α₀, equal in the case described to 50°,

radially surmounting said ply 30, a first working crown ply 31, formed of inextensible metal cables made of steel forming with the circumferential direction an angle α₁ equal to 18°, the cables of the triangulation ply 30 and of the first working ply having the same direction,

radially to the outside and in contact with the working crown ply 31, a layer P of rubber mixes, referred to as decoupling rubber, covering the end of said working ply 31,

then a second working crown ply 32 formed of metal cables identical to those of the first ply 31, and forming with the circumferential direction an angle (x2 opposed to the angle α₁ and, in the case illustrated, equal in absolute value to said angle α₁ of 18°, (but possibly being different from said angle α₁),

and finally, radially to the outside of the working crown ply 32, a last ply 33 of what are called elastic metal cables made of steel, which are oriented relative to the circumferential direction by an angle α₃ of the same direction as the angle α₂, but greater in absolute value than said angle α₂ of 8° since it is equal to 26°, this last ply being a what is called a protective ply.

The axial width L₁ of the first working ply 31 is equal to 0.78 times the maximum axial width S₀ of the centre section of the carcass reinforcement 2 when the tire is mounted on its operating rim and inflated to its recommended pressure, namely 280 mm, which, for a tire of conventional form, is less than the width of the tread, which is equal, in the case in question, to 286 mm. The axial width L₂ of the second working ply 32 is less than the width L₁, since it is equal to 212 mm. The axial width L₀ of the triangulation ply 30 is equal to 270 mm, which represents 0.75 S₀. The width L₃ of the protective ply 33 is greater than the width L₂ of the least wide and radially adjacent working ply 32, and equal to 260 mm and hence less than the width L₁.

The layer P of rubber mix ensures decoupling between the working ply 31 and the end of the radially outer working ply 32. The zone of engagement of the layer P between the two working plies 31 and 32 is defined by its thickness or more precisely the radial distance d between the end of the ply 32 and the ply 31 and by its axial width D of the layer P between the axially inner end of said layer P and the end of the radially outer working crown ply. The radial distance d is equal to 2 mm. The axial distance D is equal to 10 mm, or approximately 6 times the diameter φ₂ of the reinforcement elements of the working ply 32, the diameter φ₂ being equal to 1.65 mm.

Furthermore, the radial distance d′, such as defined previously as being the radial distance between the end of the protective ply 33 and the working crown ply 31, is equal to 3.6 mm and is hence greater than the distance d and approximately equal to d+φ₂.

The distance d″, such as defined previously as being the distance between the end of the radially inner working crown ply 31 and the protective ply, is for its part equal to 11.4 mm and hence far greater than the distance d.

FIG. 2 is a diagrammatic view in meridian section of a tire 4, similar to that of FIG. 1, which differs from the latter by the presence of a layer P of rubber mixes subdivided into two layers P₁, P₂, the layer P₁ being radially external to the layer P₂ and hence at least in contact with the radially outer working ply 32. As for the layer P₂, it is in contact with the radially inner working ply 31. The elasticity moduli at 10% elongation of the layers P₁ and P₂, respectively MP₁ and MP₂, are selected such that they satisfy the following relationship: MP₁≧MP₂. Such an embodiment of the tire 4 makes it possible to reduce the stresses in the layer P₁ of rubber mix in contact with the working ply 32 compared with the stresses of the layer P₂ of rubber mix in contact with the working ply 31, which makes it possible to improve still further the resistance of the crown structure to separation between the ends of the working plies.

FIG. 3 is a diagrammatic view in meridian section of a tire 5, similar to that of FIG. I and which differs therefrom by the presence of a layer of rubber mix GB radially to the inside of the working reinforcement. This layer of rubber mix GB is put in place such that the axially outer end of said layer GB is at a distance from the equatorial plane greater than L₁/2, L₁ being the axial width of the first working ply 31. The layer GB makes it possible in particular, due to its radially inner position in contact with the end of the working crown ply 31, to improve the resistance to propagation of cracks which may appear at the end of the working ply 31.

FIG. 4 is a diagrammatic view in meridian section of a tire 6, similar to that of FIG. 1, which furthermore comprises a ply 7 of reinforcement elements, of small diameter, which are parallel to each other in the ply and oriented radially, the axially inner edge of said additional ply 7 being radially adjacent to at least one edge of the protective ply 33 of the crown reinforcement 3, and the axially outer edge of said additional ply being radially internal to the edge of the ply to which the additional ply 7 is adjacent. The presence of such an additional ply 7 makes it possible in particular to limit the appearance of cracks between the ends of the reinforcement elements of the working plies in particular by a mechanical and thermal protection effect as explained previously.

FIG. 5 is a diagrammatic view in meridian section of a tire 8, similar to that of FIG. 1 and which differs therefrom by a ply 33′, referred to as a protective ply, of width L′₃ such that L′₃>L₁. In this configuration, the protective ply 33′ therefore has a greater width than the working ply 31; it is therefore the widest ply of the crown reinforcement. The invention advantageously provides for the distance d″, defined as being the distance between the end of the radially inner working crown ply and the supplementary ply, referred to as a protective ply, to be greater than d. The layer P of rubber mixes then acts as a decoupling layer between the radially inner working ply and the protective ply, such that the ends of the reinforcement elements of the radially inner working ply are not stressed owing to the excessive proximity of the reinforcement elements of the protective ply. As explained previously, according to the invention, the reinforcement elements advantageously do not penetrate a circle of radius d centered on the end of the reinforcement elements of the radially inner working ply. FIG. 5 shows the distance d″ in the radial direction.

Tires described in accordance with FIG. 1 were subjected to endurance testing using running on vehicles and under high drift stresses in comparison with control tires, having a protective ply which is less wide than the second working ply and formed of reinforcement elements forming with the circumferential direction the same angle as the elements of said working ply.

Whereas the control tires on average covered 6,686 km, the tires according to the invention however traveled for 11,493 km, or an increase of approximately 72%, without said tires being adversely affected by the separations observed between the two working plies.

Other tires comprising a protective ply which is wider than the radially outer working ply but not comprising a layer of decoupling rubber mixes between the working plies were also tested. Under the same conditions as for the preceding tests, these tires covered on average 10,595 km or 58% more than the control tires but 8% less than the tires according to the invention. 

1. A tire P comprising a radial carcass reinforcement radially surmounted by a crown reinforcement consisting of at least one working reinforcement formed of at least two plies of calendered inextensible metallic reinforcement elements, of rubber mix which are parallel to each other within each ply and are crossed from one ply to the next, forming angles α₁ and α₂ of between 10° and 45° with the circumferential direction, said working plies having axial widths L₁ and L₂, and of at least one supplementary ply, referred to as a protective ply, of axial width L₃ such that L₂<L₃, L₂ being the width of the working ply adjacent to the protective ply, and comprising metallic reinforcement elements, wherein a layer P of cohesive rubber mixes is arranged between at least the ends of the working crown plies.
 2. A tire according to claim 1, wherein the protective ply has a width L₃, such that L₃<L₁.
 3. A tire according to claim 1 or 2, wherein the working plies have widths L₁ and L₂, such that L₂<L₁.
 4. A tire according to claim 3, wherein the layer P, at the axially outer end of the radially outer working crown ply, has a thickness such that the radial distance d between the two working crown plies, separated by said layer P, satisfies the relationship: 3/5.φ₂ <d<5.φ₂ where φ₂ is the diameter of the reinforcement elements of the radially outer working crown ply.
 5. A tire according to claims 2 to 4, the radial distance between the two working crown plies, separated by the layer P, being equal to d, at the end of the radially outer working crown ply, wherein the end of the supplementary ply, referred to as a protective ply, is separated radially from the working crown ply of width L₁ by the layer P at a distance d′, such that: d≦d′<d+4.φ₂ where φ₂ is the diameter of the reinforcement elements of the radially outer working crown ply.
 6. A tire according to one of claims 1 to 5, the radial distance between the two working crown plies, separated by the layer P, being equal to d, at the end of the radially outer working crown ply, wherein the end of the radially inner working crown ply is distant from the supplementary ply, referred to as a protective ply, by a distance d″, such that d″≧d.
 7. A tire according to one of claims 1 to 5, wherein the widths of the working crown plies satisfy the relationship: 1>L ₂ /L ₁≧2/3.
 8. A tire according to one of the preceding claims, wherein the axial width D of the layer P between the axially inner end of said layer P and the end of the radially outer working crown ply is such that: 3.φ₂ ≦D≦20.φ₂ where φ₂ is the diameter of the reinforcement elements of the radially outer working crown ply.
 9. A tire according to one of the preceding claims, wherein the reinforcement elements of the protective ply are inclined in the same direction as the reinforcement elements of the radially adjacent working ply, forming with the circumferential direction an angle α₃ of the same direction and greater than or equal to the angle α₂ of the reinforcement elements of the working ply adjacent to the protective ply.
 10. A tire according to one of the preceding claims, wherein the angle α₃, formed by the reinforcement elements of the protective ply with the circumferential direction, is greater in absolute value than the angle α₂ of the elements of said radially adjacent working ply by at least 5°.
 11. A tire according to claim 9 or 10, wherein the angular difference α₃−α₂ is at most equal to 20°.
 12. A tire according to one of the preceding claims, wherein the crown reinforcement is finished off, radially between the carcass reinforcement and the working reinforcement, by a triangulation ply formed of inextensible metallic elements.
 13. A tire according to claim 12, wherein the inextensible metallic elements forming the triangulation ply form with the circumferential direction an angle α₀ of the same direction as the angle α₁ formed by the reinforcement elements of the radially innermost working ply and of between 45° and 90°.
 14. A tire according to one of the preceding claims, wherein the protective ply is formed of extensible steel cables.
 15. A tire according to one of the preceding claims, wherein the layer of rubber mixes P is formed of a stack of at least two layers of mix P₁ and P₂ of respective elasticity moduli MP₁ and MP₂, at 10% elongation such that MP₁>MP₂ and in that the radially outermost mix P₁ is in contact with the radially outermost working crown ply.
 16. A tire according to one of the preceding claims, wherein said tire comprises a layer of cohesive rubber mix GB radially to the inside of the working reinforcement, in that the axially outer end of said layer GB is at a distance from the equatorial plane greater than L₁/2.
 17. A tire according to claim 16, comprising a triangulation ply radially between the carcass reinforcement and the working reinforcement, wherein the layer of rubber mix GB is radially internal to said triangulation ply.
 18. A tire according to one of the preceding claims, wherein said tire comprises, at least in each shoulder, an additional ply of reinforcement elements, advantageously of small diameter, which are parallel to each other in the ply and forming with the circumferential direction an angle of between 70 and 110°, the axially inner edge of said additional ply being radially adjacent to at least one edge of one of the plies of the crown reinforcement, and the axially outer edge of said additional ply preferably being radially internal to the edge of the ply to which the additional ply is adjacent.
 19. A tire according to claim 18, wherein the axially outer edge of the additional shoulder ply is located at least in the radially upper part of the zone of the sidewall and in that the reinforcement elements of said additional ply are metallic and preferably made of steel. 